Abstract
Background
The radiotherapy can directly affect the bond strength of the adhesive materials, interfering in the prognosis of restorative treatments, which may be caused by chemical changes in dentin structure.
Methods
Twenty inferior homologues premolars were distributed in 2 groups (in vitro study) (n = 10): nonirradiated and irradiated. The specimens were submitted to the analysis of phosphate (ν1PO43−;ν2PO43−;ν4PO43−), carbonate (ν3CO32−), amide I, CH2, amide III, and amide I/III ratio by confocal Raman spectroscopy. Data were submitted to statistical analysis (T test, P < .05).
Results
In intracanal dentin, the irradiated group had lower ν4PO43− values (1.23 ± 0.06) compared to nonirradiated group (1.40 ± 0.18) (P < .05), with no difference for ν1PO43− and ν2PO43 peaks (P > .05). The irradiated (1.56 ± 0.06) had lower carbonate, amide III (1.05 ± 0.19), and amide I/III ratio values (0.19 ± 0.06) compared to nonirradiated group (1.42 ± 0.10, 1.28 ± 0.24, and 0.31 ± 0.10, respectively) (P < .05). For medium dentin irradiated group (1.30 ± 0.12) had lower phosphate values compared to nonirradiated group (1.48 ± 0.22) (P < .05). In cementum, there was no statistical difference between the groups.
Conclusion
The radiotherapy was able to cause changes in ν4PO43−, carbonate, and amide III peaks of root dentin.
https://ift.tt/2zZElky
Δεν υπάρχουν σχόλια:
Δημοσίευση σχολίου
Σημείωση: Μόνο ένα μέλος αυτού του ιστολογίου μπορεί να αναρτήσει σχόλιο.