Low-temperature co-purification of NO x and Hg 0 from simulated flue gas by Ce x Zr y Mn z O 2 /r-Al 2 O 3 : the performance and its mechanism

Abstract

In this study, series of Ce_x Zr_y Mn_z O₂/r-Al₂O₃ catalysts were prepared by impregnation method and explored to co-purification of NO_x and Hg⁰ at low temperature. The physical and chemical properties of the catalysts were investigated by XRD, BET, FTIR, NH₃-TPD, H₂-TPR, and XPS. The experimental results showed that 10% Ce_0.2Zr_0.3Mn_0.5O₂/r-Al₂O₃ yielded higher conversion on co-purification of NO_x and Hg⁰ than the other prepared catalysts at low temperature, especially at 200–300 °C. 91% and 97% convert rate of NO_x and Hg⁰ were obtained, respectively, when 10% Ce_0.2Zr_0.3Mn_0.5O₂/r-Al₂O₃ catalyst was used at 250 °C. Moreover, the presence of H₂O slightly decreased the removal of NO_x and Hg⁰ owing to the competitive adsorption of H₂O and Hg⁰. When SO₂ was added, the removal of Hg⁰ first increased slightly and then presented a decrease due to the generation of SO₃ and (NH₄)₂SO₄. The results of NH₃-TPD indicated that the strong acid of 10% Ce_0.2Zr_0.3Mn_0.5O₂/r-Al₂O₃ improved its high-temperature activity. XPS and H₂-TPR results showed there were high-valence Mn and Ce species in 10% Ce_0.2Zr_0.3Mn_0.5O₂/r-Al₂O₃, which could effectively promote the removal of NO_x and Hg⁰. Therefore, the mechanisms of Hg⁰ and NO_x removal were proposed as Hg (ad) + [O] → HgO (ad), and 2NH₃/NH₄⁺ (ad) + NO₂ (ad) + NO (g) → 2 N₂ + 3H₂O/2H⁺, respectively.

Graphical abstract

ᅟ